Influencia de la temperatura de curado en la resistencia a la compresión del hormigón y parámetros mecánicos: módulo de elasticidad y coeficiente de Poisson

Cadena Tuquinga, Andrea Belén; Palacios Lagos, Pedro Alejandro

Por favor, use este identificador para citar o enlazar este ítem: http://bibdigital.epn.edu.ec/handle/15000/17265

Registro completo de metadatos

Campo DC	Valor	Lengua/Idioma
dc.contributor.author	Cadena Tuquinga, Andrea Belén	-
dc.contributor.author	Palacios Lagos, Pedro Alejandro	-
dc.date.accessioned	2017-05-03T13:39:04Z	-
dc.date.available	2017-05-03T13:39:04Z	-
dc.date.issued	2017-04-28	-
dc.identifier.citation	Cadena Tuquinga, A. B., & Palacios Lagos, P. A. (2017). Influencia de la temperatura de curado en la resistencia a la compresión del hormigón y parámetros mecánicos: módulo de elasticidad y coeficiente de Poisson. 186 hojas. Quito : EPN.	es_ES
dc.identifier.other	T-IC/0762/CD 7770	-
dc.identifier.uri	http://bibdigital.epn.edu.ec/handle/15000/17265	-
dc.description	El presente proyecto de investigación se realiza con el propósito de analizar la influencia que tiene la temperatura de curado en las propiedades mecánicas del hormigón; mediante el ensayo de probetas cilíndricas curadas por inmersión en agua en condiciones controladas de temperatura, con valores de 10 a 40°C. Para llevar a cabo este análisis, se determinó una mezcla patrón, con una resistencia característica a la compresión de (210Kg/cm2) mediante el método recomendado por el American Concrete Institute (ACI 318S, 2005). Se pudo determinar que la temperatura de curado, bajo condiciones de laboratorio y cumpliendo los procedimientos establecidos en la normativa vigente, influye directamente en el endurecimiento del hormigón, a mayor temperatura de curado, el hormigón puede desarrollar mayor resistencia inicial.	es_ES
dc.description.abstract	The present research Project was carried out with the purpose of analyzing the influence of the curing temperature on the mechanical properties of concrete; by the test of cylindrical specimens cured in water under controlled temperature conditions, with values of 10 to 40°C. To carry out this analysis, the material characterization was carried out and a standard mixture with a characteristic compressive strength of (210 Kg/cm2) was determined by the method recommended by the American Concrete Institute (ACI 318S, 2005). It was possible to determine that the curing temperature, under laboratory conditions and complying with the procedures established in the current regulations, directly influence the hardening of the concrete, the higher the curing temperature, the concrete can develop greater initial strength.	es_ES
dc.description.sponsorship	Luna Hermosa, Germán Vinicio, director	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Quito, 2017.	es_ES
dc.rights	openAccess	es_ES
dc.subject	ESTRUCTURAS (CONSTRUCCION)	es_ES
dc.subject	HORMIGONES	es_ES
dc.subject	ENSAYO DE MATERIALES	es_ES
dc.title	Influencia de la temperatura de curado en la resistencia a la compresión del hormigón y parámetros mecánicos: módulo de elasticidad y coeficiente de Poisson	es_ES
dc.type	bachelorThesis	es_ES
Aparece en las colecciones:	Tesis Ingenieria Civil y Ambiental (ICA)

Ficheros en este ítem:

Fichero	Descripción	Tamaño	Formato
CD-7770.pdf		16,04 MB	Adobe PDF	Visualizar/Abrir

Muestra el registro sencillo del ítem

BIBDIGITAL