Por favor, use este identificador para citar o enlazar este ítem: http://bibdigital.epn.edu.ec/handle/15000/17383
Registro completo de metadatos
Campo DCValorLengua/Idioma
dc.contributor.authorPilaguano Guanochanga, Jonathan Guillermo-
dc.contributor.authorVizueta Caisatoa, Pedro Julio-
dc.date.accessioned2017-06-12T18:42:05Z-
dc.date.available2017-06-12T18:42:05Z-
dc.date.issued2017-06-05-
dc.identifier.citationPilaguano Guanochanga, J. G., & Vizueta Caisatoa, P. J. (2017). Caracterización de Compuestos de Polipropileno Reforzados con Polvo de Bambú y Nanoarcillas Obtenidos Mediante Extrusión e Inyección. 132 hojas. Quito : EPN.es_ES
dc.identifier.otherT-IM/1888/CD 7820-
dc.identifier.urihttp://bibdigital.epn.edu.ec/handle/15000/17383-
dc.descriptionSe estudió la variación de propiedades mecánicas y térmicas al incorporar polvo de bambú y nanoarcillas en una matriz polimérica. Las variables fueron tamaño de partícula de bambú, contenido en peso de bambú y nanoarcillas. Los tamaños y contenidos de bambú fueron 149, 250, 595 μm y 5, 10, 15 wt%. Los contenidos de nanoarcillas fueron 0, 2.5 y 5 wt%. El compatibilizante usado fue polipropileno maleizado en 3 wt%. Los compuestos fueron obtenidos mediante extrusión e inyección. Se realizaron ensayos de tracción, flexión, impacto, dureza. La caracterización térmica incluyó ensayos de calorimetría diferencial de barrido, análisis termogravimétrico y termomecánico. La adición de polvo de bambú y nanoarcillas mejoró los módulos de elasticidad y flexión, con efectos negativos en resistencia al impacto y tracción. Los ensayos térmomecánicos indicaron baja cristalinidad al agregar bambú y nanoarcillas, aunque mejor estabilidad térmica. La mejor composición fue 15 wt% y tamaño 250 μm de bambú, y 2.5 wt% de nanoarcillas con aumentos de 85, 21, 59, 11 y 6% en módulo de elasticidad, resistencia y módulo de flexión, dureza y densidad, y disminuciones del 76 y 14% en resistencias al impacto y tracción respecto al polipropileno. Finalmente se comparó los resultados con estudios similares.es_ES
dc.description.abstractThe effects of bamboo flour and nanoclay on the mechanical and thermal properties of polypropylene matrix were investigated. Thus, bamboo particulate size, bamboo and nanoclay loadings were chosen to assess the properties. Bamboo particulate size were 140, 250 y 595 μm. Furthermore, bamboo loadings were 5, 10, and 15 wt%, and nanoclay loadings were 0, 2.5 y 5 wt%. Maleic anhydride grafted polypropylene was set at 3 wt%. The composites were prepared by extrusion and injection molding. Tensile, flexural, impact, hardness tests were carried out to get the mechanical properties. Statistical analysis was done to know the main effects. Thermal behavior was researched by differential scanning calorimetry, thermogravimetric and thermomechanical analysis. Mechanical test showed that flexural properties were enhanced by using nanoclay and bamboo, but tensile and impact got worse. Thermal tests pointed out lower performance at crystallization because of bamboo and nanoclay, but thermal degradation was improved. The specimen PP-B15-250-N2.5 got the best properties regarding to polypropylene. Its properties´ changes were 85, 21, 59, 11 and 6% at tensile modulus, flexural strength and modulus, hardness and density and, decline 76 and 14% at impact and tensile strength regarding to polypropylene. Finally, the results were compared to other researches.es_ES
dc.description.sponsorshipGuerrero Barragán, Víctor Hugo, directores_ES
dc.language.isospaes_ES
dc.publisherQuito, 2017.es_ES
dc.rightsopenAccesses_ES
dc.subjectMECANICA DE MATERIALESes_ES
dc.subjectMATERIALES COMPUESTOSes_ES
dc.titleCaracterización de Compuestos de Polipropileno Reforzados con Polvo de Bambú y Nanoarcillas Obtenidos Mediante Extrusión e Inyecciónes_ES
dc.typebachelorThesises_ES
Aparece en las colecciones:Tesis Mecánica (IM)