dc.identifier.citationSánchez Meneses, E. F. (2020). Procedimiento y caracterización de soldadura en materiales con alto contenido de carbono equivalente (Ceq mayor 0.4%). 122 hojas. Quito : EPN.es_ES
dc.identifier.otherT-IM/2111/CD 10392-
dc.identifier.urihttp://bibdigital.epn.edu.ec/handle/15000/20869-
dc.descriptionEl presente trabajo aborda el Procedimiento y Caracterización de la soldadura en materiales con alto contenido equivalente de carbono (Ceq mayor 0.4%), utilizando el proceso de soldadura FCAW. El trabajo se lleva a cabo desde el punto de vista estructural y metalúrgico. Para la etapa experimental, se consideran parámetros como intensidad de corriente y la consideración del precalentamiento, estas medidas se consideran para obtener un buen cordón de soldadura, la verificación de los mejores parámetros se realiza con pruebas no destructivas tales como: inspección visual en cada placa, tintas penetrantes y radiografías, también se realizará pruebas destructivas: análisis metalográfico, dureza, pruebas de tracción, flexión de la cara y la raíz. En los aceros anti abrasivo, los fabricantes consideran el precalentamiento con la composición química y el grosor de la placa, este trabajo se encontró una relación según el grado de dureza. Las mejores condiciones de soldadura son con precalentamiento, debido a la alta dureza del acero utilizado en este trabajo.es_ES
dc.description.abstractThis work addresses the Procedure and Characterization of welding in materials with high carbon equivalent content (Ceq greater than 0.4%), using the FCAW welding process. The work is carried out from the structural and metallurgical point of view. For the experimental stage, parameters such as current intensity and consideration of preheating are considered, these measures are considered to obtain a good weld bead, the verification of the best parameters is carried out with non-destructive tests, stories such as: visual inspection on each plate, penetrating inks and x-rays, destructive tests are also performed: metallographic analysis, hardness, tensile tests, flexion of the face and the root. In the anti-abrasive steels, the manufacturers considered the preheating with the chemical composition and the thickness of the plate, this work found a relationship according to the degree of hardness. The best welding conditions are with preheating, due to the high hardness of the steel used in this jobes_ES
dc.description.sponsorshipGranja Ramírez, Mario German, directores_ES
dc.language.isospaes_ES
dc.publisherQuito, 2020.es_ES
dc.rightsopenAccesses_ES
dc.subjectMATERIALESes_ES
dc.subjectCARBONOes_ES
dc.subjectSOLDADURAes_ES
dc.titleProcedimiento y caracterización de soldadura en materiales con alto contenido de carbono equivalente (Ceq mayor 0.4%)es_ES
dc.typebachelorThesises_ES
Aparece en las colecciones:Tesis Mecánica (IM)

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
CD 10392.pdf11,67 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.