Análisis comparativo de las propiedades mecánicas de juntas soldadas de acero ASTM A572 tratadas térmicamente

Campos Terán, Juan Carlos; Jaramillo Flores, Luis Eduardo

Por favor, use este identificador para citar o enlazar este ítem: http://bibdigital.epn.edu.ec/handle/15000/19931

Registro completo de metadatos

Campo DC	Valor	Lengua/Idioma
dc.contributor.author	Campos Terán, Juan Carlos	-
dc.contributor.author	Jaramillo Flores, Luis Eduardo	-
dc.date.accessioned	2019-02-06T18:49:47Z	-
dc.date.available	2019-02-06T18:49:47Z	-
dc.date.issued	2019-01-10	-
dc.identifier.citation	Campos Terán, J.C. & Jaramillo Flores, L.E. (2019). Análisis comparativo de las propiedades mecánicas de juntas soldadas de acero ASTM A572 tratadas térmicamente. 98 hojas. Quito : EPN.	es_ES
dc.identifier.other	T-IM/2012/CD 9385	-
dc.identifier.uri	http://bibdigital.epn.edu.ec/handle/15000/19931	-
dc.description	En el presente trabajo se desarrolló un análisis comparativo de algunas propiedades mecánicas de juntas soldadas tratadas térmicamente en acero estructural ASTM A572 Gr. 50. Aplicando la Norma AWS D1.1 se realizaron las probetas de soldadura, es decir, se estableció los procedimientos de soldadura (WPS) para realizar los respectivos cordones. En base a la norma ASME Sección VIII División I se realizó el tratamiento térmico post-soldadura de recocido a una de las probetas, a otra probeta se le realizó un revenido de alivio de esfuerzos, y una tercera probeta no se le realizo ningún tratamiento térmico; a cada probeta se le efectuó ensayos de tracción, Charpy, barrido de dureza, doblado, y ultrasonido. En base a los diferentes ensayos fue posible determinar la variación de la microestructura y de las propiedades mecánicas (dureza, ductilidad, tenacidad) entre las juntas soldadas, para así llegar a la conclusión de que los tratamientos térmicos post-soldadura en juntas con espesores mayores a 38 [mm] son necesarios.	es_ES
dc.description.abstract	In this project a comparative analysis of some mechanical properties of welded joints treated thermally in structural steel ASTM A572 Gr.50 was developed. The welding specimens were made applying the AWS D1.1 standard. That is, the specimens and the WPS to make the respective welds were set. Based on the ASME Section VIII Division I standard, the postweld heat treatment of annealing was performed on one of the test pieces, another test piece was subjected to a stress relief temper, and a third test piece was not subjected to any heat treatment. Each test piece was subjected to tensile tests, Charpy, hardness scanning, bending, and ultrasound. Based on the different tests it was possible to determine the variation of the microstructure and the mechanical properties (hardness, ductility, toughness) between the welded joints, in order to reach the conclusion that postweld heat treatment in joints with thicknesses greater than 38 [mm] is necessary.	es_ES
dc.description.sponsorship	Barragán Campos, Galo Homero, director	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Quito, 2019.	es_ES
dc.rights	openAccess	es_ES
dc.subject	TRATAMIENTO TÉRMICO	es_ES
dc.subject	PROPIEDADES MECÁNICAS	es_ES
dc.title	Análisis comparativo de las propiedades mecánicas de juntas soldadas de acero ASTM A572 tratadas térmicamente	es_ES
dc.type	bachelorThesis	es_ES
Aparece en las colecciones:	Tesis Mecánica (IM)

Ficheros en este ítem:

Fichero	Descripción	Tamaño	Formato
Tesis.pdf		7,63 MB	Adobe PDF	Visualizar/Abrir

Muestra el registro sencillo del ítem

BIBDIGITAL