Análisis de los efectos causados por irradiación de un haz de electrones de 1 a 10 keV sobre películas de grafeno.

Moyano Quishpe, Karla Estefanía

Por favor, use este identificador para citar o enlazar este ítem: http://bibdigital.epn.edu.ec/handle/15000/23694

Registro completo de metadatos

Campo DC	Valor	Lengua/Idioma
dc.contributor.author	Moyano Quishpe, Karla Estefanía	-
dc.date.accessioned	2023-03-27T20:07:28Z	-
dc.date.available	2023-03-27T20:07:28Z	-
dc.date.issued	2023-03	-
dc.identifier.citation	Moyano Quishpe, K.E.(2023). Análisis de los efectos causados por irradiación de un haz de electrones de 1 a 10 keV sobre películas de grafeno. 59 páginas. Quito : EPN.	es_ES
dc.identifier.other	T-MVE 1013/CD 13004	-
dc.identifier.uri	http://bibdigital.epn.edu.ec/handle/15000/23694	-
dc.description	Los materiales basados en grafeno son ampliamente estudiados en la actualidad debido a las propiedades únicas que poseen. En el presente trabajo de investigación se sintetizó óxido de grafeno mediante la exfoliación electroquímica de láminas de grafito. Con el material obtenido, se elaboraron películas delgadas sobre vidrio y se irradiaron con un haz de electrones variando la energía desde 0.5 keV a 10 keV. Se observó una reducción de la resistencia laminar en las películas irradiadas cuando la energía de los electrones aumenta. De esta manera, se obtuvo una reducción máxima de 17.28 % de la resistencia laminar cuando se irradió una muestra con 10 keV durante 30 min. La relación ID/ID’ estuvo por debajo de 3.5 para todos los espectros Raman antes y después de la irradiación, lo que mostró la existencia de defectos de borde presentes en el óxido de grafeno. Mientras que, en la mayoría de los casos, la relación ID/IG se reduce cuando se aumenta la energía de irradiación. Por otro lado, los espectros FTIR y XPS mostraron una reducción de los grupos funcionales oxigenados después de la irradiación. Los resultados sugieren que existe una reducción del óxido del grafeno después de la irradiación con el haz de electrones, lo que aumenta la conductividad del material.	es_ES
dc.description.abstract	Graphene-based materials are currently widely studied due to their unique properties. In the present research work, graphene oxide was synthesized by electrochemical exfoliation of graphite sheets. With the obtained material, thin films were made on glass and irradiated with an electron beam varying the energy from 0.5 keV to 10 keV. A reduction in sheet resistance was observed in the irradiated films when the energy of the electrons increased. In this way, a maximum reduction of 17.28 % of the sheet resistance was obtained when a sample was irradiated with 10 keV for 30 min. The ID/ID' ratio was below 3.5 for all Raman spectra before and after irradiation, which showed the existence of edge defects present in graphene oxide. Whereas, in most cases, the ID/IG ratio is reduced when the irradiation energy is increased. On the other hand, FTIR and XPS spectra showed a reduction of oxygenated functional groups after irradiation. The results suggest that there is a reduction of graphene oxide after irradiation with the electron beam, which increases the conduction of the material.	es_ES
dc.description.sponsorship	Irribarra Cazar, Esteban Felipe, director.	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Quito : EPN, 2023.	es_ES
dc.rights	openAccess	es_ES
dc.subject	ELECTRONES	es_ES
dc.subject	ÓXIDO DE GRAFENO	es_ES
dc.subject	RESISTENCIA LAMINAR	es_ES
dc.subject	MECÁNICA	es_ES
dc.title	Análisis de los efectos causados por irradiación de un haz de electrones de 1 a 10 keV sobre películas de grafeno.	es_ES
dc.type	bachelorThesis	es_ES
Aparece en las colecciones:	Tesis Maestría en Materiales, diseño y producción (FC)

Ficheros en este ítem:

Fichero	Descripción	Tamaño	Formato
CD 13004.pdf		1,53 MB	Adobe PDF	Visualizar/Abrir